Survival of Zirconia- and Metal-Supported Fixed Dental Prostheses: A Systematic Review

Purpose: The aim of this review was to systematically evaluate and compare the frequency of veneer chipping and core fracture of zirconia fixed dental prostheses (FDPs) and porcelain-fused-to-metal (PFM) FDPs and determine possible influencing factors. Materials and Methods: The SCOPUS database and International Association of Dental Research abstracts were searched for clinical studies involving zirconia and PFM FDPs. Furthermore, studies that were integrated into systematic reviews on PFM FDPs were also evaluated. The principle investigators of any clinical studies on zirconia FDPs were contacted to provide additional information. Based on the available information for each FDP, a data file was constructed. Veneer chipping was divided into three grades (grade 1 = polishing, grade 2 = repair, grade 3 = replacement). To assess the frequency of veneer chipping and possible influencing factors, a piecewise exponential model was used to adjust for a study effect. Results: None of the studies on PFM FDPs (reviews and additional searching) sufficiently satisfied the criteria of this review to be included. Thirteen clinical studies on zirconia FDPs and two studies that investigated both zirconia and PFM FDPs were identified. These studies involved 664 zirconia and 134 PFM FDPs at baseline. Follow-up data were available for 595 zirconia and 127 PFM FDPs. The mean observation period was approximately 3 years for both groups. The frequency of core fracture was less than 1% in the zirconia group and 0% in the PFM group. When all studies were included, 142 veneer chippings were recorded for zirconia FDPs (24%) and 43 for PFM FDPs (34%). However, the studies differed extensively with regard to veneer chipping of zirconia: 85% of all chippings occurred in 4 studies, and 43% of all chippings included zirconia FDPs. If only studies that evaluated both types of core materials were included, the frequency of chipping was 54% for the zirconia-supported FDPs and 34% for PFM FDPs. When adjusting the survival rate for the study effect, the difference between zirconia and PFM FDPs was statistically significant for all grades of chippings (P = .001), as well as for chipping grade 3 (P = .02). If all grades of veneer chippings were taken into account, the survival of PFM FDPs was 97%, while the survival rate of the zirconia FDPs was 90% after 3 years for a typical study. For both PFM and zirconia FDPs, the frequency of grades 1 and 2 veneer chippings was considerably higher than grade 3. Veneer chipping was significantly less frequent in pressed materials than in hand-layered materials, both for zirconia and PFM FDPs (P = .04). Conclusions: Since the frequency of veneer chipping was significantly higher in the zirconia FDPs than PFM FDPs, and as refined processing procedures have started to yield better results in the laboratory, new clinical studies with these new procedures must confirm whether the frequency of veneer chipping can be reduced to the level of PFM.