Purpose: To compare the effect of office, home, and internal bleaching on the shear bond strength (SBS) of enamel to porcelain laminate veneers.
Materials and Methods: A total of 36 extracted maxillary central incisors were randomly assigned to four groups: (1) no bleaching (control); (2) office bleaching with 40% hydrogen peroxide (HP); (3) home bleaching with 15% carbamide peroxide; and (4) intracoronal bleaching with sodium perborate (SP) using the walking bleaching technique. All teeth were separately immersed in artificial saliva for 14 days. The enamel surface was then reduced by 0.5 mm, and IPS e.max Press ceramic discs were bonded using a resin cement. After 24 hours, all specimens were thermocycled (5,000 cycles, 5°C to 55°C). The SBS was measured using a universal testing machine, and the failure mode was determined using a stereomicroscope. One-way ANOVA and Tukey honest significant difference tests were used for data analysis (P < .05).
Results: A significant difference was noted among the groups (P < .001). The highest SBS was noted in the control group (15.71 ± 5.39 MPa). The mean SBS in the office bleaching group (12.30 ± 4.64 MPa) was almost the same as the control. The lowest mean SBS belonged to the home bleaching group (5.39 ± 3.99 MPa). The mode of failure was adhesive in all four groups.
Conclusion: If bleaching is intended to be followed by porcelain veneers, the office bleaching technique with 40% HP is recommended. Delaying the bonding procedure for 2 weeks does not appear to be effective with home or intracoronal bleaching.