A Polymethyl Methacrylate-Based Acrylic Dental Resin Surface Bound with a Photoreactive Polymer Inhibits Accumulation of Bacterial Plaque

Purpose: The aim of this study was to examine the ability of a poly(2-methacryloyloxyethyl phosphorylcholine-co-n-butylmethacrylate-co-2-methacryloyloxyethyloxy-p-azidobenzoate) (PMBPAz) coating on polymethyl methacrylate (PMMA)-based dental resin to inhibit bacterial plaque formation, as well as the polymer's durability against water soaking and chemical exposure. Materials and Methods: Successful application of PMBPAz on PMMA surfaces was confirmed by x-ray photoelectron spectroscopy (XPS) and measuring the static air contact angle in water. The anti-adhesive effects to bacterial plaque were evaluated using Streptococcus mutans biofilm formation assay. The mechanical and chemical durabilities of the PMBPAz coating on the PMMA surfaces were examined using soaking and immersion tests, respectively. Results: XPS signals for phosphorus and nitrogen atoms and hydrophilic status on PMMA surfaces treated with PMBPAz were observed, indicating the presence of the polymer on the substrates. The treated PMMA surfaces showed significant inhibition of S mutans biofilm formation compared to untreated surfaces. The PMBPAz coating was preserved after water soaking and chemical exposure. In addition, water soaking did not decrease the ability of treated PMMA to inhibit biofilm formation compared to treated PMMA specimens not subjected to water soaking. Conclusion: This study suggests that PMBPAz coating may represent a useful modification to PMMA surfaces for inhibiting denture plaque accumulation.