Shear Bond Strength and Failure Types of Polymethyl Methacrylate Denture Base Resin and Titanium Treated with Surface Conditioner

This study compared the shear bond strength and failure types of a polymethyl methacrylate (PMMA) denture base resin to commercially pure (CP) titanium, Ti-6Al-4V alloy, and cobalt-chromium alloy using a metal surface conditioner. The PMMA denture base resin (5 x 5 x 5 mm3) was cured onto disks, 10 mm in diameter and 2.5-mm thick. The shear bond strength of the PMMA resin with the surface conditioner was significantly higher than that without (P .05). There was no significant difference between the types of metal. The conditioned specimens showed mixed failures, whereas the nonconditioned specimens exhibited only adhesive failure at the metal-resin interface.