Purpose: To evaluate the effects of different glass-fiber post surface treatments on the bond strength to root dentin. Materials and Methods: Fifty bovine incisors were used in this study. After removing the crowns, the teeth were endodontically treated. The roots were randomly divided into five groups according to post surface treatment. The groups were as follows: CO (Control) - no treatment; G1 - RelyX Ceramic Primer (silane) only; G2 - silane and Solobond M; G3 - silane and Scotchbond Adhesive; G4 - silane and Excite. For post cementation, RelyX Unicem was used according to the manufacturer's recommendation and the roots were stored in a light-proof container with 100% relative humidity for 24 h. The specimens were transversally sectioned. Subsequently, the cervical, middle, and apical regions of the root were positioned in a push-out device and tested at 0.5 mm/min using a universal testing machine (Instron). The data were statistically analyzed with two-way ANOVA and Tukey's post-hoc test. The fractured specimens were then observed under a stereoscopic loupe at 60X magnification. Results: No significant difference in bond strength was found among the groups that received a silane or silane plus an adhesive system (p > 0.05). However, the CO (no silane) showed the lowest bond strength. Regarding G1, G2, G3, and G4, the cervical region of the root canal attained better bond strengths than did the middle or apical regions. The most frequent failure mode occurred at the cement/dentin interface. Conclusion: Silane application may be necessary to improve the adhesion of fiber posts luted with the self-adhesive resin cement evaluated here. The application of an adhesive layer between the fiber post and resin cement did not have any influence on the bond strength when the silane coupling was previously used. Keywords: bond strength, fiber post, push-out, resin cements