DOI: 10.3290/j.jad.a32807, ID de PubMed (PMID): 25264547Páginas 429-434, Idioma: InglésChen, Ji-hua / Liu, Yan / Niu, Li-na / Lu, Shuai / Tay, Franklin R. / Gao, YuPurpose: To determine whether high-pressure air blowing during adhesive application affects the infiltration of resin comonomers and nanoleakage manifestation in the resin/dentin interface under simulated pulpal pressure.
Materials and Methods: Thirty mid-coronal dentin surfaces were bonded with an etch-and-rinse adhesive (Adper Single Bond 2) under simulated pulpal pressure. In the control group, the adhesive was thinned by ordinary air blowing with a pressure of 0.2 MPa, while in the experimental group, a high-pressure air blowing technique (pressure: 0.4 MPa) was used. All other procedures followed the manufacturer's instructions. Resin tag formation and nanoleakage in the bonding interface were evaluated with scanning electron microscopy (SEM) and transmission electron microscopy (TEM).
Results: When adhesive was thinned with high pressure air blowing, longer and more homogeneous resin tags were formed. The bonding interface demonstrated good overall morphology and integrity. Almost perfect infiltration of resin and no obvious nanoleakage were observed.
Conclusion: Thinning of adhesive with high-pressure air blowing provides a clinically feasible adjunctive procedure for better resin infiltration.
Palabras clave: bonding, nanoleakage, hybrid layer, adhesive, high-pressure blowing, infiltration