Pages 142-148, Language: EnglishVallittu, Pekka K. / NarvaThe effect of fiber reinforcement of autopolymerizing poly(met hyl methacrylate) was investigated. The impact strength of continuous E-glass fiber-poly(methyl methacrylate) composite was determined. Rectangular test specimens (n = 10 per group) were modified by incorporating an additional fiber reinforcement of untreated E-glass fibers, silanized E-glass fibers, or aramid fibers in the test specimens. Controls were either unreinforced or reinforced from the middle of the test specimen only. The impact strength of the specimens was measured by using a charpy-type pendulum impact tester after the specimens had been stored in water at 37 degrees C for 4 weeks. After the impact strength test, the length of the delamination of poly(methyl methacrylate) from the fibers was measured and plotted to the impact strength of the test specimens by using a linear regression model. The impact strength of unreinforced autopolymerizing poly(methyl methacrylate) was 7.8 kJ/m to the second power, while incorporation of glass fiber reinforcement with a fiber concentration of 12.4 wt% increased the impact strength to 74.7 kJ/m to the second power (P = .000). The additional fiber reinforcement of the test specimen did not affect the impact strength (P = .363). Delamination negatively correlated with the impact strength of the test specimens (r = -.72, P = .000). The results of this study suggest that glass fiber reinforcement enhanced the impact strength of autopolymerizing poly(methyl methacrylate), while the use of additional fiber reinforcement made of aramid or glass fibers in the test specimens did not have an effect on the impact strength.