Microtensile Bond Strengths of Composite to Dentin Treated with Desensitizer Products

Purpose: This study was designed to analyze the influence of desensitizing procedures on dentin bond strength. Materials and Methods: Forty bovine incisors were used, divided into four groups (n = 10): G1: control; G2: Gluma Desensitizer (Heraeus Kulzer); G3: Oxa-Gel (Art-Dent); G4: low-intensity laser (MMOptics). The buccal surface was wet ground flat with 180-, 400- and 600-grit silicon carbide abrasive paper to expose midcoronal dentin and create a uniform surface. After the application of the desensitizing agents to the exposed dentin, the specimens were etched with 35% phosphoric acid for 30 s, and an adhesive (Single Bond) was applied and light cured. A 4-mm high crown of composite resin (Filtek Z250) was then built up. Specimens were trimmed to an hourglass shape with cross sections of 1 mm2. Each specimen was individually fractured by a microtensile testing machine at a crosshead speed of 0.5 mm/min. The data, recorded in MPa, were analyzed with one-way ANOVA and the Duncan test (p = 0.05). Results: Specimens treated with dentin desensitizers (except Gluma) yielded significantly lower mean bond strengths than nontreated control specimens. The mean values in MPa (±SD) were: G1: 13.4 (6.2); G2: 13.2 (4.8); G3: 7.15 (4.3); G4: 7.21 (4.6). Conclusions: Among the desensitizing agents studied, only Gluma Desensitizer did not detrimentally influence the bond strength values. It is a useful material for dentin desensitization. Parole chiave: dentin, desensitizer, microtensile bond strength